DESCRIPTION
Brass is essentially copper alloyed with zinc. It is strong but easy to form, stamp or draw
which make it a common choice for a broad spectrum of applications. By varying the amount of
zinc content it is possible to achieve a variety of characteristics including different
levels of corrosion resistance, ductility and suitability for machining.
CHEMICAL COMPOSITION
Elements |
Min (%) |
Max (%) |
Cu |
58.00 |
61.00 |
Pb |
0.25 |
0.70 |
Fe |
- |
0.15 |
Total Others |
- |
0.40 |
Zn |
Remainder |
MECHANICAL PROPERTIES ACCORDING TO ASTM B981 (AS PER TEMPER HO2)
Range (Inch)
|
From |
To |
UTS Min (ksi) |
PS Min (ksi) |
Elongation Min (%) |
Hardness Min (HRB) |
Hardness Max (HRB) |
Round (Dia) |
0.059 |
0.500 |
63 |
28 |
10 |
- |
- |
0.500 |
1.000 |
55 |
26 |
12 |
- |
- |
1.000 |
2.000 |
48 |
24 |
20 |
- |
- |
2.000 |
2.952 |
45 |
20 |
25 |
- |
- |
Hex (A/F) |
0.118 |
0.500 |
63 |
28 |
10 |
- |
- |
0.500 |
1.000 |
55 |
26 |
12 |
- |
- |
1.000 |
2.000 |
48 |
24 |
20 |
- |
- |
2.000 |
2.756 |
45 |
20 |
25 |
- |
- |
Square (A/F) |
0.118 |
0.500 |
63 |
28 |
10 |
- |
- |
0.500 |
1.000 |
55 |
26 |
12 |
- |
- |
1.000 |
2.000 |
48 |
24 |
20 |
- |
- |
2.000 |
2.362 |
45 |
20 |
25 |
- |
- |
Range (mm)
|
From |
To |
UTS Min (MPa) |
PS Min (MPa) |
Elongation Min (%) |
Hardness Min |
Hardness Max |
Round (Dia) |
1.5 |
12 |
430 |
190 |
10 |
- |
- |
12 |
25 |
380 |
180 |
12 |
- |
- |
25 |
50 |
330 |
165 |
20 |
- |
- |
50 |
75 |
310 |
135 |
25 |
- |
- |
Hex (A/F) |
3 |
12 |
430 |
190 |
10 |
- |
- |
12 |
25 |
380 |
180 |
12 |
- |
- |
25 |
50 |
330 |
165 |
20 |
- |
- |
50 |
70 |
310 |
135 |
25 |
- |
- |
Square (A/F) |
3 |
12 |
430 |
190 |
10 |
- |
- |
12 |
25 |
380 |
180 |
12 |
- |
- |
25 |
50 |
330 |
165 |
20 |
- |
- |
50 |
60 |
310 |
135 |
25 |
- |
- |
PHYSICAL
PROPERTIES |
Melting Point - Liquidus°F |
1650 |
Melting Point - Solidus°F |
1630 |
Density lb/cu in. at 68°F |
0.304 |
Specific Gravity |
8.41 |
Electrical Conductivity % IACS at 68°F |
28 |
Thermal Conductivity Btu/ sq ft/ ft hr/ °F at 68°F |
71 |
Coefficient of Thermal Expansion 68-57210⁻⁶ per °F (68 – 572°F) |
11.6 |
Specific Heat Capacity Btu/ lb /°F at 68°F |
0.09 |
Modulus of Elasticity in Tension ksi |
15000 |
Modulus of Rigidity ksi |
5600 |
FABRICATION
PROPERTIES |
Technique |
Suitability |
Soldering |
Excellent |
Brazing |
Good |
Oxyacetylene Welding |
Fair |
Gas Shielded Arc Welding |
Fair |
Coated Metal Arc Welding |
Not Recommended |
Spot Weld |
Not Recommended |
Seam Weld |
Not Recommended |
Butt Weld |
Fair |
Capacity for Being Cold Worked |
Fair |
Capacity for Being Hot Formed |
Excellent |
Machinability Rating |
60 |
TYPICAL USES
- Automotive
- Building Hardware
- Consumer
- Electrical
- Fasteners
- Industrial
- Ordance
- Plumbing